Polymers Materials Library
Info
- - Excellent mechanical & chemical properties
- - Excellent surface finish
- - High printability
- - Food contact approved
Details
Density
1,25 g/cm ASTM D792
Tensile Strength
47 MPa ASTM D638
Elogation at break
150% ASTM D638
Izod impact strength
No breaK ASTM D256
Heat distortion temperature
80oC ASTM D648
Info
- - Chemical & wear resistance
- - Used in electrical and electronic components
- - Good functionality under temperature
- - Food contact approved
Details
Density
1,4 g/cm ISO 1183
Tensile Strength
200 MPa ISO 527
Heat distortion temperature
240oC ISO 75
Info
- - Excellent outdoor resistance
- - Excellent surface finish
- - Good dimensional stability
- - Production of functional parts
Details
Density
1,07 g/cm ASTM D792
Tensile Strength
40 MPa ASTM D638
Tensile Modulus
1726 MPa ASTM D638
Elogation at break
35% ASTM D638
Izod impact strength
441 J/m ASTM D256
Vicat softening temperature
94oC ASTM D1525
Heat distortion temperature
86/96oC ASTM D648
Info
- - Elastic material
- - Good tear strength in all directions
- - Chemical & abrasion resistance
- - Used in electrical and electronic components
Details
Density
1,20 g/cm ISO 1183-1
Tensile Strength
49 MPa DIN 53504
Tensile Modulus
7,5/16 MPa DIN 53504
Elogation at break
600% DIN 53504
Info
- - High impact resistance
- - Excellent surface quality
- - High printability
- - Food contact approved
Details
Density
1,05 g/cm ISO 1183
Tensile Strength
26 MPa ISO 527
Elogation at break
40% ISO 527
Izod impact strength
No breaK ISO 179eU
Vicat softening temperature
88,5/38VoC ISO 306
Heat distortion temperature
85/89oC ISO 75
Info
- - Electrical insulator & thermal resistance
- - High dimensional stability
- - Easily recycled
- - Food contact approved
Details
Density
0,96 g/cm ISO 1183A
Tensile Strength
1400 MPa ISO 527
Tensile Modulus
1400 MPaISO 527
Elogation at break
20% ISO 527
Info
- - Excellent mechanical properties
- - Used in parts subjected to wear
- - Food contact approved
Details
Density
1,3 g/cm
Info
- - Excellent surface finish
- - Corrosion resistance
- - High tensile strength and hardness
- - Used in electrical and electronic components
Details
Density
1,35 g/cm 10-LA 022
Tensile Strength
49 MPa 10-LA 049
Elogation at break
13,1% 10-LA 049
Vicat softening temperature
71 oC ISO 306
Info
- - Excellent surface finish
- - High printability
- - Biodegradable by composting
- - Food contact approved
Details
Density
1,4 g/cm ASTM D792
Tensile Strength
60/32 MPa ASTM D882
Tensile Modulus
3600 MPa ASTM D882
Elogation at break
6% ASTM D882
Izod impact strength
16 J/m ASTM D256
Heat distortion temperature
55oC ASTM E2092
Info
- - Good surface finish
- - Production of functional parts
Details
Density
1,04 g/cm ISO 1183
Tensile Strength
39/32 MPa ISO 527
Elogation at break
20% ISO 527
Izod impact strength
24/10 kJ/m ISO 180+1A
Vicat softening temperature
103/96oC ISO 306
Heat distortion temperature
81oC ISO 75-A